风格1130 - 适用于300 LB ASME / ANSI管法兰的全面垫圈
亚博体彩注册菲尔普斯在许多行业中提供大量应用的垫片材料,包括水处理,炼油厂,食品加工,发电厂和其他工业应用。虽然1/8“和1/16”是最常用的柔软,但我们携带各种厚度可供选择。
Commonly Ordered Materials
Ethylene Propylene, EPDM
垫圈,密封和垫圈
筒仓和储存罐密封
天气剥离和屋顶材料
Bumpers, architectural & window seals
Medical equipment seals, electrical connector seals
Condensate tubing for HVAC equipment, Compressor Grommets
电子和电气设备密封,以及户外电气围栏
50 Durometer:ASTM D 2000 3BA 508 C12,SAE J200 3BA 508 C12,MIL R-3065 RS 508 C1
60 Durometer:ASTM D 2000 3BA 608 C12, SAE J200 3BA 608 C12, MIL R-3065 RS 608 C1
70 Durometer:ASTM D 2000 3BA 708 C12,SAE J200 3BA 708 C12,MIL R-3065 RS 708 C1
Ozone, UV, saltwater and weather.
Water, steam, and oxidating environments
非常好的低温柔性
良好的冲击和耐磨性
液压磷酸盐和硅酸盐,碱,酸取决于型和强度
2.6 lb (60 durometer EPDM)
2.7磅(70个硬度计EPDM)
NOVATEC 825F Engineered Graphite
一张优质的蒸汽板,最适用于法兰
High temperature sealing applications
ASTM F 104.(用1/32“厚度的测试)
F 38 B蠕动放松
22小时212°F(100°C):15%
22Hrs @ 392°F (200°C):35%
F 37 A Sealability
燃料A @ 14.5 PSI /垫片负载1000 psi:0.25毫升/小时
F 37 B密封性
燃料a @ 9.8 psi /垫片负载500 psi: 0.5 ml/hr
氮@ 30 psi /垫片负载3000 psi: 0.1 ml/min
F 146厚度增加
Oil #3, 5 Hrs @ 300°F:<3%
燃料B,5小时@ 73°F:<4%
F 36压缩性
@ 5000 psi垫片载荷: 45%
Recovery:10%
DIN 3535 Part 6 Gas Permeability
Nitrogen @ 580 PSI/Gasket Load 4640 PSI:2 cc / min
DIN 52913 Stress Relaxation @ 7250 PSI
16 Hrs @ 347°F: Stress Retained> 6500 PSI
16 Hrs @ 572°F: Stress Retained> 5000 PSI
DIN 3754 48 HRS @ 75°F厚度增加
H2S0.4.Sulfuric Acid 65% Concentration:7%
NaOH Sodium Hydroxide 25% Concentration: 3%
NOVATEC 925F工程石墨
Works best in high pressure flanges, pump casings, heat exchangers, lids, vessels, valve bodies and sight glasses
ASTM F104 (Tests 1/32" Thick)
F 38B蠕变放松:
22hours @ 212°F (100°C): 12%
22小时@ 392°F(200°C):30%
F 37A密封性:
燃料A @ 14.5 PSI /垫片负载1000 PSI:.20 ml / hr
F 37B Sealability
燃料A @ 9.8 PSI /垫片负载500 PSI:.06 ml / hr
氮@ 30 psi /垫片负载3000 psi: .075 ml/min
F 146厚度增加:
Oil #3, 5 Hrs @ 300°F: < 2%
燃料B,5小时@ 73°F:<1%
F 36压缩性:
5000 PSI Gasket Load, 15% F 36A Recovery: 40%
DIN 3535 Part 6 Gas Permeability:
氮@ 580 psi /垫片载荷4640 psi:.02 cc / min
DIN 52913压力放松@ 7250 PSI:
16小时347°F:压力保留> 6500 psi
16 HRS @ 572°F:保留应力> 5000 psi
DIN 3754 48 HRS @ 75厚度增加H2S04
Sulfuric Acid 65% Concentration: 6%
Na0H Sodium Hydroxide 25% Concentration: .5%
Compressed Aramid Fiber With Buna-N Nitrile Binder
适用于饮用水应用(法兰垫圈)
扭矩保持耐高温蠕变
150磅,300磅,蒸汽应用特别好
ASTM F 104.(Tests 1/32" Thick)
F 38 B蠕动放松
22小时212°F(100°C):9.3%
22小时@ 392°F(200°C):16.9%
F 146厚度增加
Oil #3, 5 Hrs @ 300°F: 5% - 7%
燃料B,5小时@ 73°F:5% - 7%
F 36A
Compressibility @ 5000 PSI Gasket Load: 8.5% +/- 1%
恢复:57%
DIN 3535 Part 6 Gas Leak Rate
Nitrogen @ 580 PSI/Gasket Load 4640 PSI: .05 cc/min
DIN 52913 Stress Relaxation @ 7250 PSI
16 Hrs @ 347°F: > 5220 PSI (36 MPA)
16 HRS @ 572°F:> 4060 psi(28 MPa)
Hot Compression Test (1/16" Thickness Used For Testing)
7250 PSI @ 68°F(20°C):总计8.2%
7250 PSI @ 572°F(300°C): 15%
丁腈粘合剂对各种油,石油衍生物提供良好的抵抗力
具有扭矩保持的高温蠕变的抵抗力提供了其密封性能